High Performance Digital Calendered Film with FLITE Technology®

Fusion Wrap featuring FLITE Technology® can be the product of choice in various situations: when cost-driven opportunities are presented, if shorter to medium term durability is specified, or when a flat to simple curve vehicle wrap application is present. A polymeric film specifically designed for vehicle wraps, the thin and flexible film facilitates ease of use and efficiency. The lite initial contact adhesive system from FLITE Technology® will ensure repositionability, developing a quick anchor tack to speed up installations.

Arlon SLX Wrap Media

Ideal for full or partial vehicle and fleet wraps, and large decals.
Fast, easy application for the novice and experienced installers.
Vibrant and reliable print quality on Eco-Solvent, Solvent, UV and Latex print systems.
Easy liner release maintaining the integrity of the graphic.

Property	Test Methods	Typical Value
Surface Finish	Gloss Meter 60° Reflection	70 to 90 Gloss Units
Thickness	Micrometer, Federal Bench Type	2-mil (50 micron)
Tensile Strength	Tensile Tester with 2-in (51 mm) jaw separation; crosshead speed of 12 in/min. (5.1 mm/s), web direction	≥ 4.5 lb/in	≥ 0.8 kg/cm
Elongation	Instron Tensile Tester as above	Average 190%
Shelf Life (In Box)	Ideal Storage Temperature 70°F (21°C) and 50% relative humidity	2 years from factory shipment
Application Temperature Range	On clean, dry substrate	40°F to 100°F	4.4°C to 38°C
Application Temperature Range	On clean, dry substrate (corrugated with rivets and channels)	60°F to 100°F	15°C to 38°C
Service Temperature Range	On clean, dry substrate	-40°F to 176°F	-40°C to 80°C
Dimensional Stability	158°F (70°C), 48 hours	0.010 in	0.24 mm
Peel Adhesion	PSTC-1, 15 min, 70°F (21°C)	≥ 2.4 lb/in	≥ 420 N/m
Peel Adhesion	PSTC-1, 24 hours, 70°F (21°C)	≥ 3.0 lb/in	≥ 525 N/m
Peel Adhesion	PSTC-1, 1 week, 70°F (21°C)	≥ 4.2 lb/in	≥ 736 N/m
Liner Release	TLMI Release at 90˚, 300 in/min (760 cm/min)	50 g/2 in	9.84 g/cm
Liner Weight	On a clean, dry substrate	0	0